Basic Info.
Model NO.
BS-ZCC
Composition
>64% Zro2, 30-35% Sio2
Bulk Density
2.5g/cm3
Specific Density
4.0g/cm3
Transport Package
Plastic Bags
Specification
0.6-6mm
Trademark
BESTN
Origin
China
HS Code
6914100000
Production Capacity
5000kg/Month
Product Description
Zirconium Silicate Ceramic Beads are made of high-grade and nanometre Yttria Stabilized Zirconia (YSZ) . This advanced precursor material guarantees excellent mechanical properties, outstanding wear resistance and good corrosion resistance. This high density zirconia ceramic bead is used to achieve maximum milling results at minimum product contamination rates. This Yttrium stabilized zirconium beads suitable for vertical stirred mill, horizontal rolling ball mill, vibrating mill and all kinds of high speed wire rod pin sand mill, etc., for all kinds of requests and cross contamination of slurry and powder, wet and dry ultrafine dispersing and grinding.
Made with micron and sub nanometer sized raw materials and advanced processes, all technical indicators and performance meet international advanced levels. 1. The sphere has good overall roundness, smooth surface, and a pearl like luster.
2. It has excellent toughness, impact resistance, and does not break during high-speed operation.
3. The wear resistance of zirconia beads is 30-50 times that of glass beads.
4. Zirconia beads have a higher density than other grinding beads and have extremely high grinding efficiency, increasing the solid content of the material or increasing the material flow rate.
5. Corrosion resistant, wear-resistant, grinding nanometer materials and dispersion, rod pin type, turbine type Sander matching.
6. PPM grade wear prevents cross contamination between beads and base materials, and does not contain heavy metals, effectively ensuring the purity of materials such as traditional Chinese medicine and chemical engineering during the grinding process.
The application fields are as follows:Mainly used for ultra-fine grinding and dispersion of materials that require "pollution" and high viscosity and hardness.
Such as: Electroceramics, nano materials, magnetic materials, silicon oxide, lithium powder, paint, color paste, paint, dye, ink, pigment, paper making, cosmetics, food, resin, adhesive, lotion, medicine, petroleum, pesticide, daily chemical and other special chemical industries.
Applicable equipment: bar pin horizontal Sander, turbine horizontal Sander, profiled dispersion disc Sander, ring Sander, centrifugal Sander, basket Sander, nano Sander and other equipment.
Such as: Electroceramics, nano materials, magnetic materials, silicon oxide, lithium powder, paint, color paste, paint, dye, ink, pigment, paper making, cosmetics, food, resin, adhesive, lotion, medicine, petroleum, pesticide, daily chemical and other special chemical industries.
Applicable equipment: bar pin horizontal Sander, turbine horizontal Sander, profiled dispersion disc Sander, ring Sander, centrifugal Sander, basket Sander, nano Sander and other equipment.
| Item | Craft | Component | Proportion | Bulk specific gravity | Moh's hardness | Abrasion | Compressive strength |
| Zirconia bead | Sintering process | Zro2:94.6% Y2O3:5.2% | 6.0 | 3.8 | 9 | <10ppm/hr (24hr) | >2300KN (Φ2.0mm) |
| Size | 0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.4-0.6mm 0.6-0.8mm 0.8-1.0mm 1.0-1.2mm 1.2-1.4mm 1.4-1.6mm 1.6-1.8mm 1.8-2.0mm 2.0-2.2mm 2.2-2.4mm 2.4-2.6mm 2.6-2.8mm 2.8-3.0mm 3.0-3.5mm 3.5-4.0mm 4.0-4.5mm 4.5-5.0mm 5.0-5.5mm 5.5-6.0mm 6.0-6.5mm 6.5-7.0mm customized | ||||||